物理性能 |
比重 |
|
ASTM D-792 |
1.16 |
23/23℃ |
|
熔体流动速率 |
200℃ 5kg |
ASTM D-1238 |
3.0 |
g/10min |
|
|
机械性能 |
IZOD冲击强度 |
1/8" |
ASTM D-256 |
20 |
kg.cm/cm |
|
IZOD冲击强度 |
1/8" |
ASTM D-256 |
3.7 |
ft.lb/in |
|
|
引张强度 |
|
ASTM D-638 |
430 |
kg/cm2 |
|
|
IZOD冲击强度 |
1/4〃 |
ASTM D-256 |
15 |
kg.cm/cm |
|
|
弯曲弹性率 |
|
ASTM D-790 |
3.2×105 |
lb/in2 |
|
|
弯曲强度 |
|
ASTM D-790 |
660 |
kg/cm2 |
|
|
弯曲强度 |
|
ASTM D-790 |
9370 |
lb/in2 |
|
|
洛氏硬度 |
|
ASTM D-785 |
102 |
R |
|
|
IZOD冲击强度 |
1/4〃 |
ASTM D-256 |
2.8 |
ft.lb/in |
|
|
伸长率 |
|
ASTM D-638 |
20 |
% |
|
|
引张强度 |
|
ASTM D-638 |
6100 |
lb/in2 |
|
|
弯曲弹性率 |
|
ASTM D-790 |
2.3×104 |
kg/cm2 |
|
|
热性能 |
热变形温度 |
|
ASTM D-648 |
96(205) |
℃ |
|
热变形温度 |
|
ASTM D-648 |
81(178) |
℉ |
|
|
|