物理性能 |
泰伯磨耗量 |
H 18轮 |
ASTM D-1044 |
168 |
mg/1000rev |
|
|
泰伯磨耗量 |
CS-17轮 |
ASTM D-1044 |
13 |
mg/1000rev |
||
|
比重 |
|
ASTM D-792 |
1.20 |
|
||
|
熔体流动速率 |
|
ASTM D-1238 |
11 |
g/10min |
||
|
机械性能 |
拉伸力 |
5%伸长 |
|
ASTM D-638 |
3.8 |
MPa |
|
10%伸长 |
|
ASTM D-638 |
6.0 |
MPa |
||
|
初耐撕裂性能 |
|
ASTM D-1004 |
94 |
kn/m |
||
|
断裂拉伸力 |
|
ASTM D-638 |
20.7 |
MPa |
||
|
埃佐冲击强度 |
23℃ |
ASTM D-256 |
不破裂 |
J/m |
||
|
硬度计硬度 |
|
ASTM D-2240 |
47 |
|
||
|
断裂伸长 |
|
ASTM D-638 |
275 |
% |
||
|
揉曲模量 |
23℃ |
ASTM D-790 |
117 |
MPa |
||
|
热性能 |
维卡软化点 |
|
ASTM D-1525 |
174 |
℃ |