耐磨焊丝
HB-YD114(Q)
1.6
50-55
(受强烈冲击后
After high impact)
高锰钢堆焊焊丝,受强烈冲击后,表面具有加工硬度的特点。
High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
HB-YD115(Q)
1.6
50-55
(受强烈冲击后After high impact)
用于受严重冲击高锰钢堆焊,加工硬化效果显著。
Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
HB-YD165(Q)
1.6
60-65
高硬度耐磨焊丝,适用于磨粒磨损表面堆焊
High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
HB-YD114(Q)
1.6
50-55
(受强烈冲击后
After high impact)
高锰钢堆焊焊丝,受强烈冲击后,表面具有加工硬度的特点。
High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
HB-YD115(Q)
1.6
50-55
(受强烈冲击后After high impact)
用于受严重冲击高锰钢堆焊,加工硬化效果显著。
Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
HB-YD165(Q)
1.6
60-65
高硬度耐磨焊丝,适用于磨粒磨损表面堆焊
High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.