EP310D
Resin type	Polypropylene, Impact Copolymer
Description	"Moplen" EP310D is a low fluidity heterophasic copolymer designed for extrusion applications where smooth processability and high mechanical properties are of the utmost importance. Main applications are extrusion of film for heavy duty applications, adhesive tapes, lamination film and extrusion blow moulded containers for e.g. detergents. "Moplen" EP310D is suitable for food contact.
Availability	Europe, Africa-Middle East

Technical data
Haze	48 % (50)
Secant modulus MD	500 MPa
Tensile StreMD	63 MPa
Tensile StreMD	16 MPa
Elongation at break MD	830 %
Density	0.900 g/cm³
Melt flow rate (MFR)	0.95 g/10 min (230°C/2.16Kg)
Tensile Modulus	1090 MPa (1 mm/min)
Tensile Stress at Yield	26.0 MPa (50 mm/min)
Tensile Strain at Break	700 % (50 mm/min)
Tensile Strain at Yield	13 % (50 mm/min)
Charpy notched impact strength	4.20 kJ/m² (-20 °C)
Charpy notched impact strength	24 kJ/m² (0 °C)
Charpy notched impact strength	79 kJ/m² (23 °C)
Heat deflection temperature B (0.45 MPa) Unannealed	83 °C
Vicat softening temperature	150 °C (A50 (50°C/h 10N))
Shore hardness	62 (Shore D)
Gloss	17 (50)