HIPS MP6500 台湾化学纤维股份有限公司
中耐冲性,用于文具,玩具,家电零件,衣架,时钟壳,FRP携配.
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | --- | ASTM D-1238 | 7.0 | g/10min |
| 机械性能 | 抗张强度 | --- | ASTM D-638 | 270(26) | kg/cm2(MPa) |
| 抗张模数 | --- | ASTM D-638 | 1.6(1570) | kg/cm2×104(MPa) | |
| 伸长率 | --- | ASTM D-638 | 35 | % | |
| 弯曲强度 | --- | ASTM D-790 | 550(54) | kg/cm2(MPa) | |
| 弯曲模数 | --- | ASTM V | 2.6(2550) | kg/cm2×104(MPa) | |
| Izod冲击强度 | --- | ASTM D-256 | 6.5(64) | kg-cm/cm(J/m) | |
| 热 性 能 | 伟氏软化点 | --- | ASTM D-1525 | 95 | ℃ |
| 热变形温度 | --- | ASTM D-1525 | 89 | ℃ | |
| 燃烧性 | 1/16" | UL 94 | NC | HB | |
| 其它性能 | 残留单体 | --- | --- | 700 | ppm max |