广州市邦懋新材料技术有限公司不仅是专业的Noryl PPO 原料供应商，亦注重技术支持及全方位的解决方案，提供从材料鉴定、模具设计、成型加工等系列帮助，亦可为客户量身定制各特殊性能之Noryl PPO 材料，进而协助客户提高产品竟争力。
NORYL PPO MX6119物性表
Will be commercialized as IGN5531. 20% glass reinforced PPE+PS. Automotive ignitions systems: coil formers, insulators. Japanese translation material.
TYPICAL PROPERTIES (1)
MECHA NICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min
88
MPa
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min
88
MPa
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min
2
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min
2
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
6090
MPa
ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span
144
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
5570
MPa
ASTM D 790
IMPACT
Value Unit Standard
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C
411
J/m
ASTM D 4812
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
85
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C
1
J
ASTM D 3763
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
155
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火
155
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
148
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
3.42E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
6.48E-05
1/°C
ASTM E 831
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.21
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm
0.1 - 0.3
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm / 模塑收缩量，横向，3.2 mm
0.3 - 0.5
%
SABIC Method
Melt Flow Rate / 熔流率, 300°C/5.0 kgf
5.2
g/10 min
ASTM D 1238
NORYL PPO MX6119物性表
Will be commercialized as IGN5531. 20% glass reinforced PPE+PS. Automotive ignitions systems: coil formers, insulators. Japanese translation material.
TYPICAL PROPERTIES (1)
MECHA NICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min
88
MPa
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min
88
MPa
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min
2
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min
2
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
6090
MPa
ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span
144
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
5570
MPa
ASTM D 790
IMPACT
Value Unit Standard
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C
411
J/m
ASTM D 4812
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
85
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C
1
J
ASTM D 3763
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
155
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火
155
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
148
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
3.42E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
6.48E-05
1/°C
ASTM E 831
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.21
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm
0.1 - 0.3
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm / 模塑收缩量，横向，3.2 mm
0.3 - 0.5
%
SABIC Method
Melt Flow Rate / 熔流率, 300°C/5.0 kgf
5.2
g/10 min
ASTM D 1238