类别： PBT PDR4908
生产厂商：美国通用电气公司
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hr | ASTM D-570 | 0.07 | % |
| 物理性能 | 模具收缩率 | 3.2mm | ASTM D-955 | 0.1-0.3 | % |
| 比重 | --- | ASTM D-792 | 1.60 | --- | |
| 模具收缩率 | 3.2mm | ASTM D-955 | 0.7-0.9 | % | |
| 阻燃性 | --- | UL 94 | 0.84 | mm | |
| 机械性能 | IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 108 | J/M |
| 拉伸强度 | --- | GEP J Method | 1100 | kgf/cm2 | |
| 拉伸强度 | --- | GEP J Method | 107 | MPa | |
| 断裂伸长率 | --- | GEP J Method | 6 | % | |
| 弯曲强度 | --- | ASTM D-790 | 1590 | kgf/cm2 | |
| 弯曲强度 | --- | ASTM D-790 | 155 | MPa | |
| 弯曲模量 | --- | ASTM D-790 | 82500 | kgf/cm2 | |
| 弯曲模量 | --- | ASTM D-790 | 8090 | MPa |