| LZOD缺口冲击强度 | 23℃ 3.2mm 或 6.4mm | ASTM D-256 | 55 或 35 | Kg.cm/cm | |
| 拉伸强度 | 23℃ | ASTM D-638 | 500 | Kg/cm2 | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 60 | % | |
| 弯曲强度 | 23℃ | ASTM D-790 | 750 | Kg/cm2 | |
| 弯曲模量 | 23℃ | ASTM D-790 | 21000 | Kg/cm2 | |
| 加工性能 | 熔融指数 | 230℃*10Kg | ASTM D-1238 | 13 | g/10min |
| 成型收缩率 | 23℃ | ASTM D-955 | 0.5~0.7 | % | |
| 热 性 能 | 热变形温度 | 6.4mm 1.82MPa | ASTM D-648 | 100 |